 產(chǎn)品詳細(xì)介紹 |
|
項(xiàng) 目 \ 牌 號(hào) |
RDL127 |
RDL130 |
RDL135 |
RDL140 |
RDL145 |
RDL150 |
RDL155 |
| Al2O3 % |
≥50 |
≥60 |
≥65 |
≥65 |
≥65 |
≥75 |
≥75 |
| 顯氣孔率 % |
≤23 |
≤22 |
≤22 |
≤22 |
≤21 |
≤21 |
≤20 |
| 體積密度 g/cm3 |
2.3～2.5 |
2.3～2.5 |
2.35～2.55 |
2.4～2.6 |
2.5～2.7 |
2.65～2.85 |
2.65～2.85 |
| 常溫耐壓強(qiáng)度 Mpa |
≥50 |
≥55 |
≥55 |
≥55 |
≥60 |
≥60 |
≥60 |
| 重?zé)�變化率 % |
1450℃×2h
0.1～-0.4 |
1450℃×2h
0.1～-0.4 |
1450℃×2h
0.1～-0.4 |
1450℃×2h
0.1～-0.2 |
1550℃×2h
0.1～-0.2 |
1550℃×2h
0.1～-0.2 |
1550℃×2h
0.1～-0.2 |
蠕變率
(0.2Mpa×50h) %
|
1270℃
≤0.8 |
1300℃
≤0.8 |
1350℃
≤0.8 |
1400℃
≤0.8 |
1450℃
≤0.8 |
1500℃
≤0.8 |
1550℃≤0.8 | |
|
項(xiàng) 目 \牌 號(hào) |
RDL127A |
RDL130A |
RDL135A |
RDL140A |
RDL145A |
RDL150A |
RDL155A |
| Al2O3 % |
≥48 |
≥50 |
≥55 |
≥60 |
≥65 |
≥70 |
≥75 |
| Fe2O3 % |
≤1.3 |
≤1.2 |
≤1.2 |
≤1.1 |
≤1.0 |
≤0.8 |
≤0.6 |
| TiO2 % |
≤1.5 |
≤1.4 |
≤1.2 |
≤1.2 |
≤1.0 |
≤0.8 |
≤0.6 |
| 顯氣孔率 % |
≤18(19) |
≤18 |
≤18(20) |
≤19(21) |
≤19(21) |
≤19(21) |
≤19(21) |
| 體積密度 g/cm3 |
≥2.25(2.22)
|
≥2.3(2.25)
|
≥2.35(2.30)
|
≥2.40(2.35)
|
≥2.50(2.45)
|
≥2.55
|
≥2.6
|
| 常溫耐壓強(qiáng)度 Mpa |
≥40(35) |
≥45(40) |
≥45(40) |
≥45(40) |
≥50(45) |
≥55 |
≥55 |
荷重軟化溫度 (0.2Mpa) T0.5
|
≥1450 |
≥1480 |
≥1550 |
≥1580 |
≥1600 |
≥1650 |
≥1650 |
重?zé)�變化率 %
|
1450℃×2h
±0.2 |
1350 ℃×4h
±0.2 |
1400 ℃×4h
±0.2 |
1400 ℃×4h
±0.2 |
1500 ℃×4h
±0.2 |
1500 ℃×4h
±0.2 |
1500 ℃×4h
±0.2 |
0.2Mpa蠕變率 %
(20~50h) |
1270℃
≤0.2 |
1300℃
≤0.2 |
1350℃
≤0.2 |
1400℃
≤0.2 |
1450℃
≤0.2 |
1500℃
≤0.2 |
1550℃
≤0.2 | | | |
|